Analyse der Struktur von aktiven Füllstoffen mittels Streumethoden

URN to cite this document: urn:nbn:de:bvb:355-opus-6583

Schneider, Gerald Johannes (2006) Analyse der Struktur von aktiven Füllstoffen mittels Streumethoden. PhD, Universität Regensburg

Preview

Publishing license for publications excluding print on demand
PDF - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader
6Mb

Abstract (German)

Im Rahmen der Dissertation wurde die Struktur von aktiven Füllstoffen mittels Röntgen- und Neutronenkleinwinkelstreuexperimenten untersucht. Dabei stand die Analyse von Streuexperimenten an Kieselsäure in verstreckten Elastomeren im Vordergrund. Insbesondere gelang in diesem Zusammenhang die analytische Ableitung eines Ausdrucks, der die Berechnung von Streudiagrammen von anisotropen Strukturen erlaubt. Durch einen Vergleich mit experimentellen Ergebnissen, die am DESY Hamburg gewonnen wurden, konnten die theoretischen Vorhersagen bestätigt werden.

Ferner wurde im Rahmen der Arbeit die Struktur von Kieselsäure in undeformierten Elastomerproben untersucht. Als experimentelle Parameter wurden der Füllstoffanteil, das Silan und das Elastomer variiert. Dabei konnte belegt werden, dass die Struktur der Agglomerate der Kieselsäure nur sehr wenig von den genannten Variablen abhängt.

Zusätzlich wurde die Genauigkeit der Ergebnisse analysiert. In diesem Zusammenhang wurde zum einen der Einfluss der Probenzusammenstellung auf die Streudiagramme untersucht. Zum anderen wurde die Abhängigkeit der Ergebnisse vom verfügbaren Streulängenbereich nachgewiesen.

Translation of the abstract (English)

Within the context of the Ph. D. thesis the structure of active fillers was investigated by means of small angle X-ray and small angle neutron scattering experiments. The main focus was put on analyzing scattering experiments of precipitated silica in stretched elastomers. Concerning this subject an analytical expression for calculating the scattering diagrams of anisotropic structures was derived. Due to a comparison with experimental results conducted at DESY Hamburg the theoretical predictions were confirmed.

Furthermore, the structure of precipitated silica in unstretched elastomers was investigated. For this purpose the filler degree, the silane and the elastomers were varied. It was shown that the structure of the silica clusters depends only to a few extend on the mentioned variables.

In addition, the accuracy of the results was analyzed. Concerning this topic, on the one hand the influence of the ingredients of the mixtures was investigated. On the other hand, the dependence of the results on the accessible scattering length scales was demonstrated.

Item Type:

Thesis of the University of Regensburg (PhD)

Referee:

Dietmar (Prof. Dr.) Göritz

Date of exam:

26 April 2006

Institutions:

Physics > Institute of Experimental and Applied Physics > Retired Professors > Group Dietmar Göritz

Classification:

Notation	Type
61.10.Dp	PACS
61.10.Eq	PACS
61.10.Nz	PACS
61.12.Ex	PACS
61.12.Ld	PACS

Keywords:

Kleinwinkelstreuung , Röntgen-Kleinwinkelstreuung , Kieselsäuren , Neutronenstreuung , Agglomerat , Agglomerieren , Streutheorie , Elastomer , Füllstoff , Silan , Struktur , Deformation , Streudiagramm , aktive Füllstoffe , silica , elastomers , deformation , scattering diagram , silane

Subjects:

500 Science > 530 Physics

Status:

Published

Refereed:

Yes, this version has been refereed

Created at the University of Regensburg:

Yes

Owner:

Universitätsbibliothek Regensburg

Deposited On:

27 Oct 2009 08:47