Chipping of implant-supported molar crowns (iSCs) is a frequently reported complication. This study aimed to investigate the in-vitro aging and fracture resistance of iSCs with a CAD/CAM resin composite veneer structure fabricated with the Rapid Layer Technology (RLT) approach. Eight iSCs per group were fabricated by using two different CAD/CAM resin composites (Shofu Block HC: SH; Grandio blocs: GB) for veneer structures, and zirconia (ZrO2), polyetheretherketone (PEEK), and cobalt-chromium (CoCr; control) as framework materials. The surfaces to be bonded were sandblasted, cleaned in an ultrasonic bath, and a coupling agent was applied. A self-adhesive resin luting composite was used to adhesively lute the veneer structures to the frameworks. The crowns were semi-permanently cemented to the abutments. After storage in deionized water, iSCs were loaded in a chewing simulator (TCML, 10,000 thermal cycles 5 degrees C to 55 degrees C for 20 s, 1.2 million, loading force 50 N). Four ZrO2 and one CoCr crown did not survive the TCML. The fracture force was determined after 24 h storage in deionized water and yielded values of >= 974 N. Lowest fracture forces were yielded in the PEEK-SH group in comparison to CoCr or ZrO2 groups (p <= 0.031). For identical framework materials, no significant influence of the veneering material was observed. All PEEK-GB frameworks fractured, and chipping occurred for ZrO2-SH and all CoCr frameworks. PEEK-SH and ZrO2-GB presented both chipping and framework fractures. Within the limitations of this in-vitro study, the RLT with a CAD/CAM resin composite veneer structure might be a promising approach to veneer iSCs. Yet, the choice of the CAD/CAM resin composite and of the framework material determine the fracture resistance.