| Item type: | Article | ||||
|---|---|---|---|---|---|
| Journal or Publication Title: | Dental Materials | ||||
| Publisher: | ELSEVIER SCI LTD | ||||
| Place of Publication: | OXFORD | ||||
| Volume: | 27 | ||||
| Number of Issue or Book Chapter: | 8 | ||||
| Page Range: | pp. 796-804 | ||||
| Date: | 2011 | ||||
| Institutions: | Medicine > Lehrstuhl für Zahnärztliche Prothetik | ||||
| Identification Number: |
| ||||
| Keywords: | FIXED-PARTIAL DENTURES; OCCLUSAL TOOTH WEAR; IN-VITRO WEAR; 2-BODY WEAR; LABORATORY SIMULATION; LAYER STRUCTURES; DENTAL CERAMICS; HUMAN-ENAMEL; ZIRCONIA; STRENGTH; Wear; Zirconia; Porcelain; Ceramics; Pin-on-block; Glaze; All-ceramic | ||||
| Dewey Decimal Classification: | 600 Technology > 610 Medical sciences Medicine | ||||
| Status: | Published | ||||
| Refereed: | Yes, this version has been refereed | ||||
| Created at the University of Regensburg: | Yes | ||||
| Item ID: | 64746 |
Web of ScienceAbstract
Aim. The aim of this in vitro study was to compare the two-body wear resistance of substructure zirconia and veneering porcelain versus steatite and human enamel antagonists, respectively. Materials and methods. Two-body wear tests were performed in a chewing simulator with steatite and enamel antagonists (enamel cusps). A pin-on-block design with a vertical load of 50 N for 1.2 x 10(5) cycles; ...
Abstract
Aim. The aim of this in vitro study was to compare the two-body wear resistance of substructure zirconia and veneering porcelain versus steatite and human enamel antagonists, respectively. Materials and methods. Two-body wear tests were performed in a chewing simulator with steatite and enamel antagonists (enamel cusps). A pin-on-block design with a vertical load of 50 N for 1.2 x 10(5) cycles; (f = 1.6 Hz; lateral movement: 1 mm, mouth opening: 2 mm) was used for the wear test. For quantification of the wear resistance, wear tests were performed with standardized steatite spheres. Human enamel was used as a reference. Five zirconia ceramics and four veneering porcelains were investigated. One zirconia ceramic was tested with superficial glaze, which was applied after polishing or sandblasting, respectively. Surface roughness R(a) (SP6, Perthen-Feinpruf, G) and wear depth were determined using a 3D-Profilometer (Laserscan 3D, Willytec, G). SEM (Quanta FEG 400, FEI, USA) pictures were used for evaluating wear performance of both, ceramics and antagonists. Results. No wear was found for zirconia substructures. Veneering porcelain provided wear traces between 186.1 +/- 33.2 mu m and 232.9 +/- 66.9 mu m (steatite antagonist) and 90.6 +/- 3.5 mu m and 123.9 +/- 50.7 mu m (enamel). Wear of the steatite antagonists varied between 0.812 +/- 0.256 mm(2) and 1.360 +/- 0.321 mm(2) for zirconia and 1.708 +/- 0.275 mm(2) and 2.568 +/- 0.827 mm(2) for porcelain. Enamel generally showed wear, cracks or even fractures at the ridge, regardless whether opposed by zirconia or porcelain/glaze. Enamel was polished, when opposed to zirconia, or plowed, provoked and grinded, when opposed to porcelain/glaze. Conclusion. The results of the wear test with steatite or enamel antagonists indicated no measurable wear on zirconia surfaces. Porcelain showed higher wear than zirconia, but comparable or lower wear than an enamel reference. Antagonistic wear against zirconia was found to be lower than wear against porcelain. (C) 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.