Two new ternary Pt-rich phosphides, EuPt6P2 and EuPt3P, have been prepared via a two-step solid state reaction. Their crystal structures have been determined from powder XRD data. EuPt6P2 is isostructural to SrPt6P2 (cubic, Pa3, a = 8.4603(1) angstrom); its crystal structure comprises corner-sharing Pt6P trigonal prisms hosting Eu2+ cations in the cuboctahedral voids of the framework. EuPt3P is ...
Zusammenfassung
Two new ternary Pt-rich phosphides, EuPt6P2 and EuPt3P, have been prepared via a two-step solid state reaction. Their crystal structures have been determined from powder XRD data. EuPt6P2 is isostructural to SrPt6P2 (cubic, Pa3, a = 8.4603(1) angstrom); its crystal structure comprises corner-sharing Pt6P trigonal prisms hosting Eu2+ cations in the cuboctahedral voids of the framework. EuPt3P is isostructural to the SrPt3P anti-perovskite (P4/nmm, a = 5.7452(1) angstrom and c = 5.4212(1) angstrom). Magnetization measurements reveal the magnetic response caused by the Eu2+(4f 7) cations. EuPt6P2 is paramagnetic exhibiting no phase transitions down to 1.8 K, whereas EuPt3P orders ferromagnetically below 19 K. Similar to SrPt6P2 and SrPt3P, the new compounds are metallic with states near the Fermi level predominantly formed by the 5d orbitals of Pt.
Altmetric