Kojima, K. ; Funato, M. ; Kawakami, Y. ; Nagahama, S. ; Mukai, T. ; Braun, H. ; Schwarz, U. T.
Alternative Links zum Volltext:DOIVerlag
Dokumentenart: | Artikel |
---|
Titel eines Journals oder einer Zeitschrift: | Applied Physics Letters |
---|
Verlag: | AMER INST PHYSICS |
---|
Ort der Veröffentlichung: | MELVILLE |
---|
Band: | 89 |
---|
Nummer des Zeitschriftenheftes oder des Kapitels: | 24 |
---|
Datum: | 2006 |
---|
Institutionen: | Physik > Institut für Experimentelle und Angewandte Physik |
---|
Identifikationsnummer: | Wert | Typ |
---|
10.1063/1.2404971 | DOI |
|
---|
Stichwörter / Keywords: | RIDGE; |
---|
Dewey-Dezimal-Klassifikation: | 500 Naturwissenschaften und Mathematik > 530 Physik |
---|
Status: | Veröffentlicht |
---|
Begutachtet: | Ja, diese Version wurde begutachtet |
---|
An der Universität Regensburg entstanden: | Ja |
---|
Dokumenten-ID: | 69607 |
---|
Zusammenfassung
Optical gain spectra were measured for InGaN-based laser diodes (LDs) emitting at 406 nm (LD406) and 470 nm (LD470) by employing the Hakki-Paoli method. The internal loss coefficient was as large as 35 cm(-1) for the LD470 compared to 25 cm(-1) for LD406. Moreover, gain saturation was observed at about 490 nm just below the lasing threshold, and a gain band appears at higher photon energies for ...
Zusammenfassung
Optical gain spectra were measured for InGaN-based laser diodes (LDs) emitting at 406 nm (LD406) and 470 nm (LD470) by employing the Hakki-Paoli method. The internal loss coefficient was as large as 35 cm(-1) for the LD470 compared to 25 cm(-1) for LD406. Moreover, gain saturation was observed at about 490 nm just below the lasing threshold, and a gain band appears at higher photon energies for further carrier injection resulting in lasing at 470 nm. Spontaneous emission peaks of electroluminescence were measured as a function of injection current density below threshold for both samples. The authors attribute the huge blueshift of the spontaneous emission of LD470 up to 450 meV to a filling of the localized tail states in addition to that caused by the screening of the piezoelectric field. The blueshift for the LD406 was as small as about 30 meV and can be interpreted as a result of the screening by both injected carriers and dopants. (c) 2006 American Institute of Physics.